NAPAC2016 - List of Authors (Xin, T.)

Paper	Title	Page
WEPOB67	K2CsSb Photocathode Performance in QWR SRF Gun	1042
	E. Wang, Y. Hao, Y.C. Jing, V. Litvinenko, I. Pinayev, T. Rao, J. Skaritka, G. Wang, T. Xin BNL, Upton, Long Island, New York, USA
	In 2016 run of Coherent Electron Cooling, we have successfully tested the performance of a number of K2CsSb cathodes. These cathodes with QE of 6%-10% were fabricated in Instrumentation Division, a few miles away, transported to RHIC tunnel under UHV conditions, attached to the CeC gun, kept in storage, and inserted in the gun as needed. A maximum bunch charge of 4.6 nC was generated in the gun when the QE was 1.8 %. With careful conditioning at increasing accelerating fields, it was possible to maintain the QE of several cathodes for more than a week. For the cathodes that experienced degradation, the primary cause was multipacting when the power into the gun was increased. In the initial runs, the entire 20 mm substrate face was coated with the cathode material causing cathode induced multipacting. For subsequent measurements, the substrate was masked to coat only the central 9 mm of the substrate. By optimizing the procedure for boosting the power to the gun and covering all viewports to minimize dark current, we were able to minimize QE degradation. In this paper we discuss the cathode preparation, transfer to the gun and operational experience with the cathodes in 112 MHz gun.
DOI •	reference for this paper ※ https://doi.org/10.18429/JACoW-NAPAC2016-WEPOB67
Export •	reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml)

Paper

Title

Page

K2CsSb Photocathode Performance in QWR SRF Gun

1042

E. Wang, Y. Hao, Y.C. Jing, V. Litvinenko, I. Pinayev, T. Rao, J. Skaritka, G. Wang, T. Xin
BNL, Upton, Long Island, New York, USA

In 2016 run of Coherent Electron Cooling, we have successfully tested the performance of a number of K2CsSb cathodes. These cathodes with QE of 6%-10% were fabricated in Instrumentation Division, a few miles away, transported to RHIC tunnel under UHV conditions, attached to the CeC gun, kept in storage, and inserted in the gun as needed. A maximum bunch charge of 4.6 nC was generated in the gun when the QE was 1.8 %. With careful conditioning at increasing accelerating fields, it was possible to maintain the QE of several cathodes for more than a week. For the cathodes that experienced degradation, the primary cause was multipacting when the power into the gun was increased. In the initial runs, the entire 20 mm substrate face was coated with the cathode material causing cathode induced multipacting. For subsequent measurements, the substrate was masked to coat only the central 9 mm of the substrate. By optimizing the procedure for boosting the power to the gun and covering all viewports to minimize dark current, we were able to minimize QE degradation. In this paper we discuss the cathode preparation, transfer to the gun and operational experience with the cathodes in 112 MHz gun.