LINAC2018 - List of Keywords (background)

Paper	Title	Other Keywords	Page
TUPO071	Study on Nitrogen Infusion for 1.3 GHz SRF Cavities Using J-PARC Furnace	cavity, SRF, injection, vacuum	499
	K. Umemori, T. Dohmae, M. Egi, Y. Hori, E. Kako, T. Konomi, S. Michizono, T. Saeki, H. Sakai, Y. Yamamoto KEK, Ibaraki, Japan J. Kamiya JAEA/J-PARC, Tokai-mura, Japan S. Kurosawa, K. Takeishi JAEA, Ibaraki-ken, Japan T. Okada Sokendai, Ibaraki, Japan
	Nitrogen infusion (N-infusion) is new surface treatment technique for niobium SRF (Superconducting RF) cavities. After cooling down from 800 degree C heat treatment, a vacuum furnace and cavities are kept 120 degree C, 48 hours with about 3 Pa Nitrogen. Improvement of Q-value and accelerating gradient is expected. We used J-PARC furnace, since N-infusion procedure requires clean vacuum furnace. It has a cryo-pump and turbo molecular pumps and its vacuum system is oil-free system. Six times of N-infusion tests were carried out, while changing vacuum condition, N-infusion temperature, Nitrogen pressure, niobium material and so on. Niobium caps were mounted on cavities to avoid contaminations on inner surfaces. Some of trials were successful and vertical test results showed improvement of Q-values and accelerating gradient. However, some of them were not. Most of bad cases showed degradation of Q-values above 5 MV/m. Details of heat treatment procedure including N-infusion and vertical test results are shown in this presentation.
DOI •	reference for this paper ※ https://doi.org/10.18429/JACoW-LINAC2018-TUPO071
About •	paper received ※ 20 September 2018 paper accepted ※ 20 September 2018 issue date ※ 18 January 2019
Export •	reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml)

Paper

Title

Other Keywords

Page

TUPO071

Study on Nitrogen Infusion for 1.3 GHz SRF Cavities Using J-PARC Furnace

cavity, SRF, injection, vacuum

499

K. Umemori, T. Dohmae, M. Egi, Y. Hori, E. Kako, T. Konomi, S. Michizono, T. Saeki, H. Sakai, Y. Yamamoto
KEK, Ibaraki, Japan
J. Kamiya
JAEA/J-PARC, Tokai-mura, Japan
S. Kurosawa, K. Takeishi
JAEA, Ibaraki-ken, Japan
T. Okada
Sokendai, Ibaraki, Japan

Nitrogen infusion (N-infusion) is new surface treatment technique for niobium SRF (Superconducting RF) cavities. After cooling down from 800 degree C heat treatment, a vacuum furnace and cavities are kept 120 degree C, 48 hours with about 3 Pa Nitrogen. Improvement of Q-value and accelerating gradient is expected. We used J-PARC furnace, since N-infusion procedure requires clean vacuum furnace. It has a cryo-pump and turbo molecular pumps and its vacuum system is oil-free system. Six times of N-infusion tests were carried out, while changing vacuum condition, N-infusion temperature, Nitrogen pressure, niobium material and so on. Niobium caps were mounted on cavities to avoid contaminations on inner surfaces. Some of trials were successful and vertical test results showed improvement of Q-values and accelerating gradient. However, some of them were not. Most of bad cases showed degradation of Q-values above 5 MV/m. Details of heat treatment procedure including N-infusion and vertical test results are shown in this presentation.

DOI •

reference for this paper ※ https://doi.org/10.18429/JACoW-LINAC2018-TUPO071

About •

paper received ※ 20 September 2018 paper accepted ※ 20 September 2018 issue date ※ 18 January 2019

Export •

reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml)