MOPO130 | Magnetic Flux Generated by Thermal Current in CEBAF 5-Cell Cavity System | 273 |
|
||
The unloaded quality factor Q0 of many 5-cell CEBAF cavities were lowered by a factor of ~2 from their vertical qualification testing to their beam operation in CEBAF tunnel. Causes of this Q0 degradation were studied previously, including a more recent one addressing static fluxes arising from magnetic components near a 5-cell cavity. This paper reports on a preliminary study of the dynamic fluxes generated by a thermal current. Such a thermal current arises from the Seebeck effect and flows in closed loops formed by a niobium cavity and its surrounding tuner rods and liquid helium vessel that are made of stainless-steel. The behaviors of magnetic fluxes in response to various thermal profiles on a 5-cell CEBAF cavity with integrated tuner rods were studied in a JLAB VTA dewar. An outcome of this study is a proposed cool-down procedure for eliminating the thermal current generated magnetic fluxes around 5-cell cavities placed in CEBAF tunnels. This procedure may be useful to improve cavity Q0 in a cost-effective manner, which in turn saves cryogenic expenditures for sustaining CEBAF operation. | ||
DOI • | reference for this paper ※ https://doi.org/10.18429/JACoW-LINAC2018-MOPO130 | |
About • | paper received ※ 01 September 2018 paper accepted ※ 19 September 2018 issue date ※ 18 January 2019 | |
Export • | reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml) | |
TUPO076 | An Innovative Nb3Sn Film Approach and Its Potential for SRF Applications | 513 |
|
||
Funding: Work supported by U.S. DOE contract No. DE-AC02-07CH11359 A novel electro-chemical technique to produce Nb3Sn films on Nb substrates was developed and optimized at Fermilab. The Nb3Sn phase is obtained in a two-electrode cell, by electrodeposition from aqueous solutions of Sn layers and Cu intermediate layers onto Nb substrates. Subsequent thermal treatments in inert atmosphere are realized at a maximum temperature of 700°C to obtain the Nb3Sn superconducting phase. Several superconduct-ing Nb3Sn films were obtained on Nb substrates by study-ing and optimizing most parameters of the electro-plating process. Samples were characterized at Fermilab, NIMS, KEK and JLAB, including EPMA analyses, DC and in-ductive tests of critical temperature Tc0, and lower critical field Hc1(4.2 K) by SQUID. In parallel to sample devel-opment and fabrication at FNAL, at JLAB and KEK effort was put into etching and electro-polishing techniques adequate to remove the Cu and bronze phases from the samples’ outer surface. This is necessary prior to meas-urements at JLAB of the surface impedance of flat sam-ples in a setup that make use of an RF host cavity. |
||
DOI • | reference for this paper ※ https://doi.org/10.18429/JACoW-LINAC2018-TUPO076 | |
About • | paper received ※ 21 September 2018 paper accepted ※ 08 October 2018 issue date ※ 18 January 2019 | |
Export • | reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml) | |