MOP073	IHEP 1.3 GHz Low Loss Large Grain 9-cell Cavity Fabrication, Processing and Test	305
	J.Y. Zhai, J. Gao, S. Jin, Z.Q. Li, Y. Liu, Z.C. Liu, Z.H. Mi, X.H. Peng, T.X. Zhao, H.J. Zheng IHEP, Beijing, People's Republic of China C.A. Cooper, C.M. Ginsburg, T.N. Khabiboulline, A.M. Rowe, D.A. Sergatskov Fermilab, Batavia, USA J.X. Wang, H. Yu, H. Yuan BIAM, Beijing, People's Republic of China
	The combination of the low-loss shape and large grain niobium material is expected to be the possible way to achieve higher gradient and lower cost for ILC 9-cell cavities, and will be essential for the ILC 1 TeV upgrade. As the key component of the “IHEP 1.3 GHz SRF Accelerating Unit Project”, a low-loss shape 9-cell cavity with full end groups using Ningxia large grain niobium (IHEP-02) was fabricated at IHEP in 2012. The cavity was processed (CBP and EP) and tested at FNAL. The cavity processing,test performance and gradient limitation is reported in this paper. We will weld the helium vessel, assemble the magnetic shield and install the cavity to IHEP ILC-TC1 cryomodule.

Paper

Title

Page

IHEP 1.3 GHz Low Loss Large Grain 9-cell Cavity Fabrication, Processing and Test

305

J.Y. Zhai, J. Gao, S. Jin, Z.Q. Li, Y. Liu, Z.C. Liu, Z.H. Mi, X.H. Peng, T.X. Zhao, H.J. Zheng
IHEP, Beijing, People's Republic of China
C.A. Cooper, C.M. Ginsburg, T.N. Khabiboulline, A.M. Rowe, D.A. Sergatskov
Fermilab, Batavia, USA
J.X. Wang, H. Yu, H. Yuan
BIAM, Beijing, People's Republic of China

The combination of the low-loss shape and large grain niobium material is expected to be the possible way to achieve higher gradient and lower cost for ILC 9-cell cavities, and will be essential for the ILC 1 TeV upgrade. As the key component of the “IHEP 1.3 GHz SRF Accelerating Unit Project”, a low-loss shape 9-cell cavity with full end groups using Ningxia large grain niobium (IHEP-02) was fabricated at IHEP in 2012. The cavity was processed (CBP and EP) and tested at FNAL. The cavity processing,test performance and gradient limitation is reported in this paper. We will weld the helium vessel, assemble the magnetic shield and install the cavity to IHEP ILC-TC1 cryomodule.